Synthesis of W –TiO2 nanoparticles for enhanced dye-sensitized solar cell performance
سال انتشار: 1394
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 511
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ETEC05_061
تاریخ نمایه سازی: 19 اردیبهشت 1395
چکیده مقاله:
TiO2 nanoparaticles were prepared bysolegel method by varying different mole % of tungstan and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM). The energy-conversion efficiency of a cell based on 0.5 mol% W-doped TiO2 is significantly better, compared to that of a cell based on undoped TiO2. The enhancement of the performance of DSSCs achieved using 0.5 mol% W–TiO2 nanoparticle fims is attributable to the slower recombination time and the introduction absorption of light in the visible range and especially in the range 300–420 nm. Th above results demonstrate the potential application of introduction of W nanoparticles to improve for enhancing the performance of TiO2 nanoparticle-based DSSCs, which can be produced on a large scale at low cost
کلیدواژه ها:
نویسندگان
sajad Hosein Zadeh
Guilan distribution company, Lahijan
Maryam Ghomashpasand
Department of Chemistry, Faculty of Science, University of Guilan
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :