Effects of Hybridization of Carbon and Polypropylene Short Fibers as Reinforcement on Flexural Properties of Fine Aggregate Concretes
محل انتشار: ژورنال مهندسی عمران، دوره: 2، شماره: 10
سال انتشار: 1395
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 354
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_CEJ-2-10_003
تاریخ نمایه سازی: 6 شهریور 1396
چکیده مقاله:
Nowadays, the advantages of short fibers as reinforcement in cement based materials are well known. In this paper, the effect of hybridization of short polypropylene (PP) and carbon fibers on flexural properties of a fine aggregate concrete has been investigated. Samples with dimensions of containing 2 vol% of the polypropylene and carbon fibers with 6 and 8mm length were made. The PP to carbon fiber proportion in the samples were selected as 100:0, 75:25, 50:50, 25:75 and 0:100. A four-point bending test was carried out on all the samples to investigate the flexural behaviour. It was found that the addition of carbon fibers significantly increases the flexural load (i.e. 260%). The application of PP fibers leads to a 2590% increase in the toughness compared to the control sample. It was also found that the sample with carbon to PP ratio of 75/25 shows the optimum results and it leads to 190% and 2070% increment in the flexural load and toughness, respectively, in comparison to the control sample
کلیدواژه ها:
نویسندگان
Mana Halvaei
Textile Engineering Department, Amirkabir University of Technology, Tehran, Iran.
Masoud Jamshidi
Polymer research lab,Chemical Engineering Department, Iran University of Science and Technology (IUST), Tehran, Iran.
Masoud Latifi
Textile Engineering Department,Textile Excellence & Research Centers, Amirkabir University of Technology, Tehran, Iran.