Emulsifier- free emulsion polymerization of styrene: effect of carboxylic acid monomer type on particle nucleation and growth
محل انتشار: اولین کنفرانس پتروشیمی ایران
سال انتشار: 1387
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,697
فایل این مقاله در 16 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IPCONF01_154
تاریخ نمایه سازی: 6 آذر 1386
چکیده مقاله:
Carboxylated polystyrene latexes were prepared by emulsifier- free emulsion copolymerization of styrene with various carboxylic acid monomers (AA, MAA and IA). DLS analysis and SEM observations were used to investigate the effect of various carboxylic acid monomers on the particle formation and growth processes. It was found that number of particles per unit volume of aqueous phase ( N p ) increases with increasing hydrophobicity of carboxylic acid monomers in order of IA < AA < MAA. There was significant difference in polymerization rate per particle ( R p N p ) in all the experiments also. The results revealed that both particle nucleation and growth processes are dependent on the hydrophilic nature of carboxylic acid monomers. SEM studies showed that N p is almost constant in the particle growth stage (conversion above 10%). Through some calculations by data obtained from DLS technique, average diameter of monomer swollen polymer particles ( d pswol ) of all the carboxylated polystyrene latexes at the same conversion of 0.4 was obtained to be 325.24, 199.30 and 661.02 nm for AA, MAA and IA respectively. Attempt was made to calculate the average number of propagating radicals per particle and to determine its relevance to the kinetics of particle growth by various carboxylic acid monomers.
کلیدواژه ها:
Carboxylated polystyrene latex ، Emulsifier- free emulsion polymerization ، particle nucleation and growth ، Dynamic light scattering
نویسندگان
Mahdi Abdollahi
Research Institute of Petroleum Industry, Division of Polymer Science and Technology, Research Institute of Petroleum Industry (RIPI)
Ali Rahmatpour
Research Institute of Petroleum Industry، Division of Polymer Science and Technology, Research Institute of Petroleum Industry (RIPI),
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :