Possibility of Applying Chromium Coat on Aluminium without Interlayer and its Corrosion Behaviour
سال انتشار: 1399
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 272
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES14_020
تاریخ نمایه سازی: 1 دی 1399
چکیده مقاله:
In this research, the possibility of the applying chromium coat on a pure aluminium substrate without interlayer was investigated. It is mentioned in literature that due to the formation of oxide layer on the surface of the aluminium, interlayer is needed to apply chromium coat on it to improve the surface microhardness. Therefore, chromium coat applied by electroplating method and optimum process parameters were achieved at current density 60 A/dm2 within 45 minutes. Bright and uniform chromium coat was obtained under this condition. The surface morphology of that was studied by field emission scanning microscopy (FE-SEM) and atomic force microscopy (AFM). Finally, corrosion behavior of the optimum coat was investigated by polarization test and electrochemical impedance spectroscopy (EIS). Results show that significant improvement at corrosion resistance of the coated sample in comparison to pure aluminium where calculated corrosion rate is equal to 0.32 mpy. Also, it is seen that pitting corrosion had been occurred at the surface of the coated sample.
کلیدواژه ها:
نویسندگان
Nesa Sherkat Khabazi
Bachelor Student of Materials Engineering, Materials Engineering Department, University of Tabriz, Tabriz, Iran
Shakiba Shadi
Bachelor Student of Materials Engineering, Materials Engineering Department, University of Tabriz, Tabriz, Iran
Avrid Taghizadeh Tabrizi
PhD Candidate of Materials Engineering, Materials Engineering Department, University of Tabriz, Tabriz, Iran
Hossein Aghajani
Associate Professor of Materials Engineering, Faculty of Materials Engineering, Iran University of Science & Technology, Tehran, Iran