بررسی نانوذرات NP-MnFe2O4 به عنوان کاتالیسیت موثر برای کاتد هوا و الکترولیت سبز 1-اکتیل-3-متیل ایمیدازولیوم هگزافلوئوروفسفات [Omim][PF6 در باتری قابل شارژ لیتیم-هوا
محل انتشار: دوفصلنامه ایرانی شیمی تجزیه، دوره: 6، شماره: 2
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 769
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJAC-6-2_006
تاریخ نمایه سازی: 17 آذر 1398
چکیده مقاله:
A simple, new and low-cost design of Li-air battery was introduced. An effective synthesized nanocatalyst for modifiying of air cathode, filter paper as a simple separator and a conductive ionic liquid namely 1-Octyl-3-methyl imidazolium hexafluorophosphate abbreviated [Omim][PF6] as a non-aqueous and green electrolyte in battery were used. The MnFe2O4 nanoparticles (NP-MnFe2O4) which consistingof transition metal-metal oxide components was synthesized in our labrature. High discharge capacity, non-flammability of electrolyte, high reversibility, long lifetime and low over potential were observed in electrochemical tests of the battery. Synthesized nanocatalyst was characterized using XRD, FTIR and SEM techniques. XRD results show that a nanocatalyst have a particle sizes of 16-28 nm that distributed on cathode uniformly and performance of battery was improved to more than 1000 cycles compared to battery without any catalyst. The discharge capacity at current density of 0.2 mA cm-2 and charge potential range of 2.0-4.2 V for battery with catalyst/green electrolyte and without catalyst/common organic electrolyte were 3391 and 1012 mAh g-1,respectively. Furthermore, the usage of an ionic liquid as electrolyte leads to the increase the safety and lifetime of battery. Because of used electrolyte have high boiling point amount (> 350 Celcius), so if it released to the environment due to the destruction or life expires of battery, don’t seriously damage to the environment because it is not easily evaporated.
کلیدواژه ها:
نویسندگان
Mehdi Hosseini
Department of Chemistry, Faculty of Basic Science, Ayatollah Boroujerdi University, Boroujerd, Iran.
Mousa Soleymani
Department of Chemistry, Faculty of Basic Science, Ayatollah Boroujerdi University, Boroujerd, Iran.
Hossein Dashti Khavidaki
Department of Chemistry, Faculty of Basic Science, Ayatollah Boroujerdi University, Boroujerd, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :