Investigation of Mechanical Properties of Transient Liquid Phase bonding of Inconel738 Nickel base superalloy to TiAl Intermetallic compound
سال انتشار: 1398
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 535
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES13_072
تاریخ نمایه سازی: 13 آبان 1398
چکیده مقاله:
Transient Liquid pahse (TLP) bonding was used to join a nickel base superalloy Inconel 738 in as -cast condition to TiAl intermetallic compound by using two different interlayer MBF30 and pure Cu with 50micron thickness. TiAl intermetallic was casted of titanium and aluminum with 99.9% purity by Vacuum Arc Melting(VAR) furnace. Bonding were carried out in vacuum atmosphere at temperature range between 1120-1150 with different bonding times. Bonding microstructure was studied by light and scanning electron microscopes. Microstructural evaluation was depicted some intermetallic compounds had been appeared. With bonding at higher temperatures or bonding times has been disappeared or discontinued. By increasing bonding time, amount of eutectic structure was decreased gradually and continuous eutectic phases are disappeared at 1150 and 10 minutes. Results show that the microstructure of bond area has different complex composition and phases in spite of their discontinuities. Mechanical properties show that the hardness of the bonding area because of brittle boride and carbide phases that are formed in that area is higher than near the base materials areas. The shear strength of MBF-30 bonded samples are higher than Cu interlayer bonded samples.
کلیدواژه ها:
نویسندگان
Dariush Kokabi
Material Science Ph.D. Student at IROST
Ali Kaflou
Assistant Professor, IROST
Majid Pouranvari
Assistant Professor, Sharif University of Technology
Reza Gholamipour
Assistant Professor, IROST