Preparation and characterization of a bionanopolymer film for walnut packaging
محل انتشار: فصلنامه پلی اولفین ها، دوره: 6، شماره: 2
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 516
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_POJ-6-2_006
تاریخ نمایه سازی: 5 مرداد 1398
چکیده مقاله:
To apply the nanomaterial as a component in the packaging material structure, in this research, the carboxymethyl cellulose (CMC)/polyvinyl alcohol (PVA) film were prepared with three levels of nanoclay particles (0.5, 1 and 3%) using solution casting evaporation method. The incorporation of nanoclay on mechanical, water vapor permeability, and oxygen barrier properties of CMC/PVA-based film was investigated. The best result was obtained through the nanocomposite film contain 3% nanoclay. In the next step, the CMC/PVA/nanoclay films were employed for walnut packaging. After 90 days storage in the environmental condition, the optimum result was found through the nanocomposite film with 3% nanoclay in terms of oil content, moisture content, acidity and peroxide indexes of walnuts. According to the overall results, the reinforcement of CMC/PVA film with 3% nanoclay could be introduced as a good candidate for the development of high barrier food packaging material against the diffusion of water vapor and oxygen permeability.
کلیدواژه ها:
نویسندگان
Behjat Tajeddin
Agricultural Engineering Research Institute (AERI), Agricultural Research, Education and Extension Organization (AREEO), Karaj, Iran
Najmaeh Ramedani
Food Science and Technology Department, Food Science and Technology Faculty, Science and Research Branch, Islamic Azad University, Tehran, Iran
Habibolah Mirzaei
Food Process Engineering Department, Food Science Faculty, Gorgan University of Agricultural Sciences & Natural Resources, Gorgan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :