Experimental study of durability of concrete with different cement types subject to Freeze-Thaw cycles
سال انتشار: 1397
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 679
فایل این مقاله در 17 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CAUCONF01_0050
تاریخ نمایه سازی: 30 شهریور 1397
چکیده مقاله:
To achieve a practical and simple model for evaluating parameters on durability of concrete against freeze-thaw cycles, samples based on ASTM C666 were made. Samples were made using Three different water-cement ratios of 0.4, 0.5, and 0.6 and three Air percentages of 1.5%- entrapped air, 4.5%, and 6% entrained air. Cement types used in this study are Portland cement type 1, type 5 and Pozzolan cement. Samples were subjected to three freeze-thaw cycles of 40, 100, and 150 and then compressive strength test. The Change in length and weight of samples were measured and compared with control samples. The best experimental performance was obtained for water-cement ratio of 0.4 and 4.5% of air in samples made of Portland cement type 1. Adding air more than 4.5% of the concrete volume will reduce the durability but still is better than the non-air entrained ones.
کلیدواژه ها:
نویسندگان
Seyed Hossein Ghasemzadeh Mosavinejad
Assistant Professor at Department of civil engineering, University of Guilan, Iran
Ali Shabani Chafjiri
MSc student at Department of civil engineering, Ferdowsi university of Mashhad, Iran
Alireza Malaki Ghaleh
MSc graduate of Department of civil engineering, University of Mohaghegh Ardabili, Iran