THE INFLUENCE OF THE MECHANCAL. ALLOYNG ON THE STRUCTURAL AND MAGNETIC PROPERTIES OF NANOSTUCTURED NIFEMOT ALLOY

سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 293

فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

UFGNSM03_264

تاریخ نمایه سازی: 10 تیر 1396

چکیده مقاله:

In this work, the structural and magnetic properties of amorphous/nanocrystalline NiFeMoT powders prepared by mechanical alloying are investigated. Structural study was carried out by X-ray diffraction, high resolution transmission electron microscopy and scanning electron microscopy. At 120h, the Ni main peak is completely broad and the crystallite size is about 3 nm with a minute amount of Mo phase due to high melting point, hardness and low diffusion at low temperature of Mo in to Ni. At 190h the intensity of Ni main peak is higher and the Ti peak is creating again. The interatomic distance between transition metals (2.545 nm) and the peak shift (A2e-1.08 degree) are maximum at 120h milling. The magnetic measurement of sample milled for 120h show low magnetic permeability and high operating frequencies up to 1000 Hz.

نویسندگان

LELA KARMI

Electroceramics Group, Materials Science and Engineering Department, Shiraz University of Technology, ۷۱۵۵۵-۳۳, Shiraz, Iran

HOOMAN SHOKROLLAHI

Electroceramics Group, Materials Science and Engineering Department, Shiraz University of Technology, ۷۱۵۵۵-۳۱۳, Shirgz, Iran

ZAHRA KARMI

Materials Science and Engineering Group, Mechanic Department, Tabriz University, Tabriz, Iran.