MAGNETIC PROPERTIES OF AND-FE-B BONDED MAGNET USINGA
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 361
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_087
تاریخ نمایه سازی: 10 تیر 1396
چکیده مقاله:
Permanent magnets have been widely used in various applications for many decades to convert electrical energy into mechanical energy or vice versa. Hard magnetic nanocrystalline materials such as Nd-Fe-B alloys are a new family of magnets which show unexpected properties such as a high energy density even in an isotropic state. Principal synthesis methods of these materials include high energy ball milling, melt spinning and hydrogen assisted methods such as reactive milling and hydrogenation-disproportionation-desorption-recombination (HDDR) process. Powders prepared by melt spinning with Nd2Fe14B as the hard magnetic phase have an average grain size of 30-50 nm. This leads to development of isotropic magnetic properties. In this work, bonded magnets were produced by using a nanocrystallineNd-Fe-B powder made from a melt spinning technique. The samples were produced from a mixture of isotropic powder and an epoxy resin as binder using a compression-molding technique. The morphology and average particle size of the powders were investigated by an SEM, the average grain size of the Nd2Fe14B type phase was identified using a TEM, and the magnetic properties of the bonded magnets were measured by using a hysteresis loop tTacer.
کلیدواژه ها:
نویسندگان
NANOCR YSTALLINE POWDER
MLAD AHMADI Department of Materials Engineering, Faculty of Mechanical Engineering, University of Tabriz, Tabriz, ۵۶۶-۱۶۴۷ Iran
ABBAS KIANVASH
Department of Materials Engineering, Faculty of Mechanical Engineering, University of Tabriz,