Effect of CeO2 on thermal and structural properties of MAS glass
محل انتشار: کنفرانس بین المللی مهندسی معدن، فلزات و مواد
سال انتشار: 1394
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 619
فایل این مقاله در 15 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
MINMETALCONF01_035
تاریخ نمایه سازی: 25 آذر 1395
چکیده مقاله:
In this work, CeO2 was added to the MAS glass system at theexpense of TiO2 as nuclei. Differential thermal analysis (DTA)studies show that by CeO2 addition, the surface crystallizationtrend in MAS glass system was promoted and the crystallizationtemperature increased Up to 1000°C, but thermal expansioncoefficient (TEC) of doped glasses were decreased to4.23×10-6/°C. The optimum nucleation temperature and densitiesof nacelles were determined by means of classical SEMmethod for G8 sample. In addition, according to UV–Vis absorptionanalysis the absorption bond at 400 nm was appearedwhich can be attributed to Ce4+ in this system. Also inspite of TiO2, the CeO2 did not enter in to the MAS systemduring initial steps of crystallization and the cerium aluminatephase formed at 1300°C.
کلیدواژه ها:
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :