Study on microstructure and mechanical properties of rolled alloy 5083 H112 after heat treating at different temperatures
محل انتشار: چهاردهمین همایش صنایع دریایی
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 521
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NSMI14_155
تاریخ نمایه سازی: 12 تیر 1395
چکیده مقاله:
Generally control of micro structure for improvement of material properties is very important. Hence, several researches have been done to improve structure and mechanical behavior of materials in sub-micron grain size at recent years. Grain atomizing is an effective and economical method to improve the mechanical properties of materials. In this study a thickness reduction of about 85% was applied on Aluminum 5083 H112 sheet by cold rolling. Then samples were heat treated at different temperatures. The micro structure changes were tested by optical microscopes. In order to analyze the mechanical properties; the samples were applied to mono-axis tensile, hardness and wear tests. Also the investigation of fracture surface of samples after tensile tests and microstructure was done by SEM.The results showed that the critical temperature in micro-structure changes is 250 °c. Also at this temperature a static recrystalization takes place which starts at 200°c.The result of wear test showed that friction coefficient near to static recrystalization process increase slightly which in accordance with temperature increase it starts to decrease. Samples hardness by effect of heat treatment at 250°c, increase then it starts to decrease. Also the fracture surface results show that a mixture of tear ductile dimples at recrystalization temperature leads to rupture.
کلیدواژه ها:
نویسندگان
Saeid Akhavan
M.S.c Metallurg, Isfahan University of Technology;
Ali Saghayan nejad
M.S.c Metallurg, Isfahan University of Technology;
mohamadreza Toroghi nejad
Dr. Metallurg, Isfahan University of Technology;
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :