Strengthening of steel/Al foam sandwich tube interface through in situ synthesis of Al/Ni Intermetallics
سال انتشار: 1393
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 928
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC03_049
تاریخ نمایه سازی: 9 فروردین 1395
چکیده مقاله:
Metal- foam filled tubes as a set of thin walled sandwich structures have unique properties in which the impact energy absorption is the most important among them. It is proved that the shear strength of core-shell interface plays a decisive role on increasing the amount of energy absorbed in these kinds of structures. In this research the Al foam was fabricated using sintering-dissolution process (SDP) in situ in the tube. At the same time, a composite layer was synthesized with the aim of exothermic reaction of the formation of aluminum- Nickel intermetallic compounds during the sintering process. Furthermore, The X-Ray Diffraction and Electron Dispersive Spectroscopy(EDS) Analysis both proved the formation of diverse Nickel Aluminide's, when the optical and scanning electron microscopy evaluations exhibited a good continuity and metallurgical bonding of the core-shell interface and the structure of a Nickel Aluminide's composite which was fabricated in situ. Eventually, Microhardeness examination showed an improvement of interfacial strength in the final product
کلیدواژه ها:
Aluminium- foam filled tubes – interfacial strengthening – Nickel Aluminides - Nanostructure Intermetallic-Metal Matrix Composite (IMC)
نویسندگان
Mohammad Mahdi Baloochian
Department of Materials Science and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Mashhad, Iran
Jalil Vahdati Khaki
Department of Materials Science and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Mashhad, Iran
Seyyed Abdolkarim Sajadi
Department of Materials Science and Metallurgical Engineering, Engineering Faculty, Ferdowsi University of Mashhad, Mashhad, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :