Thermal Catalytic Cracking of Naphtha over CeO2 Supported on Multi Wall Carbon Nanotubes Coated with SiO2
محل انتشار: هفتمین کنگره ملی مهندسی شیمی
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 607
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC07_362
تاریخ نمایه سازی: 25 فروردین 1394
چکیده مقاله:
In this research Multi wall Carbon Nanotubes (MWNTs) were coated first with SiO2 and then decorated with CeO2 nano particles and vice versa. The effect of metal oxide deposition priority on increasing the thermal resistance of MWNTs was investigated and results indicated the best performance for catalyst which was coated first with CeO2. Catalysts were caracterized with XRD, SEM, TGA,and ASAP. The Performance of catalysts in thermal catalytic cracking (TCC) of naphta for production of light olefins was studied at 680oC and the steam ratio equal to 0.5; finally the results were compared with thermal cracking conditions
کلیدواژه ها:
نویسندگان
Somaye Sheybani
Department of Chemical Engineering, Tarbiat Modares University
Jafar Towfighi
Department of Chemical Engineering, Tarbiat Modares University
Ali Mohamadalizade
Gas Research Division, Research Institute of Petroleum Industry
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :