Synthesis of nanostructure ZSM-5 zeolite for gas separation membrane processes
سال انتشار: 1385
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,494
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICNPGP01_012
تاریخ نمایه سازی: 16 دی 1385
چکیده مقاله:
ZSM-5 zeolite was successfully synthesized in the present of TPAOH as an organic template by sol-gel method at 175 °C after stirring in the synthesis mixture with the molar composition of 46SiO2:Al2O3:5Na2O:2TPA:1.3Trien:2500H2O. X-ray diffraction results confirmed the formation of ZSM-5 crystal phase and scanning electron microscopy images showed a twin crystal structure for the synthesized ZSM-5 zeolite seeds. Also, the effects of crystallization time, calcination time and temperature were investigated on the crystallinity and morphology of the synthesized ZSM-5 zeolite. The obtained results showed that the first one has the most significant effect on the final product structure.
کلیدواژه ها:
نویسندگان
Karimi
۱Nanostructure Materials Research Center (NMRC), Sahand University of Technology
Babaluo
Nanostructure Materials Research Center (NMRC), Sahand University of Technology, Research Center of Polymeric Materials, Sahand University of Technology,
Bayati
Research Center of Polymeric Materials, Sahand University of Technology
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :