Simulating Atmospheric Corrosion of Sterling Alloy in Sulphuric Gasses and Effect of Adding Germanium, Using Factsage Software
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,014
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES06_409
تاریخ نمایه سازی: 8 بهمن 1391
چکیده مقاله:
Silver plate specimens with two different compositions have been exposed to the atmospheric gases H2S and SO2 in humidified air under carefully controlled laboratory conditions. Air with H2S or SO2 was passed through a circular tube which contains the specimens. Temperature and relative humidity of test condition was carefully controlled. After exposure, the corrosion product formed on the sample surfaces was analyzed with XRD thin layer(grazing). Tarnishing of specimens was measured by glossmeter. Factsage software used to simulating the corrosion condition and predicting the corrosion product composition. Resultsshow that adding Ge to sterling alloy decreases the corrosion rate and increases the tarnish resistance of specimens. Corrosion products shows difference of chemical reactions were happening during exposure. Adding Ge to sterling alloy decreasecorrosion rate and increase tarnish resitance of specimens
کلیدواژه ها:
نویسندگان
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :