The Effect of Heat Treatment on the Microstructure and Mechanical Properties of 316L Stainless Steel Coatings Deposited by Flame Thermal Spray
محل انتشار: سومین کنفرانس بین المللی عملیات حرارتی مواد
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,642
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICMH03_061
تاریخ نمایه سازی: 21 تیر 1391
چکیده مقاله:
In this research, the effects of heat treatment on the microstructure, the oxidation and mechanical properties of 316L stainless steel coatings sprayed by flame spraying process were studied. The microstructure characteristics of the deposits were studied using the combined techniques of X-ray diffraction (XRD) and scanning electron microscopy (SEM). Furthermore, the mechanical properties were tested using the adhesion strength and microhardness tests. Coatings have been heat-treated at a range of temperatures between 900 and 1150 °C. Results indicate that by heat-treating the coatings at a temperature of 900 °C, it is possible to achieve higher adhesion strength and hardness values. This was attributed to the improvements in the coating microstructure during the heat-treatment, which resulted in an improvement in coating's mechanical properties through the formation of intermediate phases, and the establishment of metallurgical bonding within the coating microstructure. However, the results also indicate that by increasing the temperature to a degree higher than 1150 °C, there was a reduction in the coating's mechanical properties. This could be attributed to the grain growth, and coarsened precipitation of the equilibrium phases from supersaturated solid solutions.
کلیدواژه ها:
نویسندگان
m Khadivi
Young Researchers Club, Najaf Abad Branch, Islamic Azad University, Najaf Abad, Isfahan, Iran
A. Shafyei
Department of Materials Eng., Isfahan University of Technology, Isfahan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :