Morphological, topographical, and mechanical characteristics of Ni-Fe alloy electrodeposits
سال انتشار: 1401
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 136
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CARSE06_059
تاریخ نمایه سازی: 26 اردیبهشت 1401
چکیده مقاله:
This paper attempts to evaluate the morphological and topographical characteristics as well as mechanical properties of Ni-Fe alloy coatings. The coatings are deposited using direct current (DC)- electrodeposition technique from a Watts bath. Morphological and topographical features of the fabricated deposits were studied by a field emission scanning electron microscope (FESEM) and atomic force microscope (AFM) respectively. The microhardness of the electrodeposits was measured by Vickers microhardness tester. The obtained results showed that the surface morphology of the alloy film is compact without any obvious defects. The AFM image confirmed the compactness of thesurface. The surface roughness and microhardness of the alloy deposit are ۳.۲۸ nm and ۳۹۵±۱۰ HV, respectively.
کلیدواژه ها:
نویسندگان
Mir Saman Safavi
MSc, Department of Materials Engineering, Faculty of Mechanical Engineering,University of Tabriz, Tabriz, Iran
Ali Rasooli
Associate Professor, Department of Materials Engineering, Faculty of Mechanical Engineering, University of Tabriz, Tabriz, Iran