Investigating the Effect of Electrical Discharge Process Input Parameters on Mechanical Properties of Aluminum Surface
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 238
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ADMTL-14-3_002
تاریخ نمایه سازی: 1 آبان 1400
چکیده مقاله:
One of the important parameters in electrical discharge machining is the presence of micro cracks on the workpiece surface (recast layer). Therefore, the aim of this study was to investigate the possibility of increasing the mechanical properties of aluminum surface by alloying elements (copper and nickel) diffusion to the recast layer and thus removing surface micro cracks. For this purpose, pulse on time and pulse current in with and without ultrasonic vibration have been considered as input parameters and the presence of surface micro cracks has been investigated using microscopic images. Also, the yield stress of the surface layer was calculated using the surface micro hardness. Based on the obtain results, surface without micro cracks has been created on the aluminum surface due to the diffusion of copper and nickel into the workpiece surface which increased aluminum surface yield strength from ۹۰MPa to ۲۸۰MPa without ultrasonic vibrations and to ۳۱۰MPa while applying ultrasonic vibrations. In other words, ultrasonic vibrations cause an average of ۲۰% increase in surface layer yield strength. In addition, according to the wear test, in the case of using ultrasonic vibration, improving the mechanical properties of the surface has caused thinner grooves on the aluminum surface.
کلیدواژه ها:
نویسندگان
Hadi Eivazi bagheri
Department of Mechanical Engineering, Babol Noshirvani University of Technology, Babol, Iran
Hamid Gorji
Department of Mechanical Engineering, Babol Noshirvani University of Technology, Babol, Iran
Mohammad Reza Shabgard
Department of Mechanical Engineering, Tabriz University, Tabriz, Iran
mohamad Bakhshi-Jooybari
Department of Mechanical Engineering, Babol Noshirvani University of Technology, Babol, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :