Investigation on Composition and Microstructural Morphology of the Fe-B-C Hardfacing Layers

سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 521

فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

JR_JEFM-3-1_001

تاریخ نمایه سازی: 25 تیر 1398

چکیده مقاله:

The application of hardfacing materials for producing wear-resistant coatings on components working in wear conditions is one of the important advices in environmental protection and increasing the service life of engineering equipment. In this study, the microstructure of the hardfaced layers made by two cored wires containing Fe-B and Fe-B-C powder-based were investigated. ST37 plain carbon steel was used as the substrate and the deposition of the hardfaced layers was conducted by the flux cored arc welding (FCAW) process under single-, two-, and three-pass conditions. The microstructural and phase analyses were carried out by field emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD), respectively. The results showed that the characteristic microstructures of the Fe-B hardfacing alloy layers comprised a matrix containing elliptical dendritic ferrite and the eutectic of (α-Fe2B). But, the Fe-B-C hardfacing alloy layers included columnar-like Fe2B, skeletal-like Fe2B, daisy like Fe3(C, B) and the eutectic of (P-Fe2B).

کلیدواژه ها:

نویسندگان

M. R. Tavakoli Shoushtari

Department of Materials Science and Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Iran

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • I. Kováč, R. Mikuš, J. Žarnovský, R. Drlička, J. Žitňanský ...
  • J. Gou, Y. Wang, J. Sun and X. Li, J. ...
  • J. Gou, P. Lu, Y. Wang, S. Liu and Z. ...
  • J. H. Kim, K. H. Ko, S. D. Noh, G. ...
  • L. Rovatti, J. N. Lemke, A. Emami, O. Stejskal and ...
  • K. Gunther, J. P. Bergmann and D. Surf. Coat. Technol., ...
  • E. O. Correa, N. G. Alcântara, L. C. Valeriano, N. ...
  • N. Yuksel and S. Sahin, Mater. Des., 2014, 58,  491. ...
  • A. Gualco, H. G. Svoboda and E. S. Surian, Wear, ...
  • M. H. Amushahi, F. Ashrafizadeh and M. Shamanian, processes. Surf. ...
  • I. Manna, J. D. Majumdar, B. R. Chandra, S. Nayak ...
  • W. Xibao, W. Xiaofeng and S. Zhongquan, Surf. Coat. Technol., ...
  • R. Zahiri, R. Sundaramoorthy, P. Lysz and C. Subramanian, Surf. ...
  • J. J. Coronado, H. F. Caicedo and A. L. Gomez, ...
  • V. V. Kozyrev, M. Petrov, L. G. Yu, and L. ...
  • J. N. Lemke, L. Rovatti, M. Colombo and M. Vedani, ...
  • K. Yang, Y. Gao, K. Yang, Y. Bao and Y. ...
  • A. Gualco, H. G. Svoboda, E. S. Surian, Weld Int., ...
  • H. Sabet, Sh. Khierandish, S. Mirdamadi and M. Goodarzi, Tribol ...
  • M. Zhuang, L. Li, J. Wang, S. Ma and S. ...
  • D. Yi, J. Xing, H. Fu, Z. Zhang, J. Chen, ...
  • J. Zhang, Y. Gao, J. Xing, S. Ma, D. Yi ...
  • Y. Jian, Z. Huang, J. Xing and B. Wang, crystals. ...
  • L. G. Yu, X. J. Chen, K. A. Khor and ...
  • M. Eroglu. Surf. Coat. Technol., (203)2009, 2229. ...
  • Y. Jian, Z. Huang, J. Xing, B. Zheng, L. Sun,Y. ...
  • A. Motallebzadeh, E. Dilektasli, M. Baydogan, E. Atar and H. ...
  • Z. Huang, J. Xing and C. Guo, Addition. Mater. Des., ...
  • D. Yi, J. Xing, Z. Zhang, H. Fu and C. ...
  • Y. K. Singla, N. Arora and D. K. Dwivedi, A ...
  • Y. Dawei, X. Jiandong, F. Hanguang, M. Shengqiang and L. ...
  • Z. Huang, J. Xing and L. Lv, Cast Alloy. Mater. ...
  • نمایش کامل مراجع