Preparation, characterization and photocatalytic degradation of methylene blue by Fe3+ doped TiO2 supported on natural zeolite using response surface methodology
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 301
فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_AET-3-4_003
تاریخ نمایه سازی: 22 تیر 1398
چکیده مقاله:
The photocatalytic degradation of methylene blue was investigated with TiO2 and Fe2O3 nanoparticles supported on natural zeolite. The synthesized photocatalyst was characterized by XRD, XRF, FT-IR, EDX, FE-SEM, and BET analyses. The results of XRD, FT-IR, and EDX confirmed the successful loading of Fe3+ doped TiO2 nanoparticles on natural zeolite. Further, the FE-SEM results confirmed the deposition of TiO2/Fe2O3 on the zeolite, with the approximate particle size being 52.3 nm. According to the XRF results, the synthesized nanoparticles had Fe3+/TiO2 molar ratios of 0.06 in the synthesized photocatalyst. Based on BET analysis, the surface area of TiO2/Fe3+/natural zeolite was about 112.69 m2/g. The effects of operational factors such as pH (6-10), dye concentration (25-75 mg/L) and H2O2 concentration (10-40 mg/L) were considered and optimized via response surface methodology utilizing Box-Behnken design. The optimization results indicated that the maximum percentage of degradation was achieved at a dye concentration of 25 mg/L, initial pH of 10, and H2O2 concentration of 40 mg/L with a 90 min irradiation time and a 1 g/l photocatalyst concentration. The dye degradation efficiency reached 92% under this optimum condition.
کلیدواژه ها:
نویسندگان
Hadieh Taghvaei
Department of Chemical Engineering, Faculty of Engineering, University of Isfahan, Isfahan, Iran
Mehrdad Farhadian
Department of Chemical Engineering, Faculty of Engineering, University of Isfahan, Isfahan, Iran
nila davari
Department of Chemical Engineering, Faculty of Engineering, University of Isfahan, Isfahan, Iran
samira maazi
Department of Chemical Engineering, Faculty of Engineering, University of Isfahan, Isfahan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :