Preparation and characterization of MWCNT-COOH/PVC ultrafiltration membranes to use in water treatment
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 373
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_AET-4-2_003
تاریخ نمایه سازی: 22 تیر 1398
چکیده مقاله:
Polyvinyl chloride (PVC) membranes containing pristine and modified multiwall carbon nanotube (MWCNT) were prepared and characterized. MWCNT was modified in order to achieve well-dispersion within the membranes. The results of FTIR analysis revealed that MWCNT was successfully carboxylated. The FESEM images indicated that the number of pores on the surface of membranes increased at the presence of pristine and modified MWCNT and the pore size distribution curves shifted towards smaller pores. The hydrophilicity, pure water flux, tensile strength and abrasion resistance of the membranes increased with increasing the content of MWCNT and COOH-MWCNT up to 0.3 wt. % and then decreased due to the agglomeration of nanotubes. Nevertheless, at the same content of nanotubes, COOH-MWCNT had more effect than MWCNT. The performance of the membranes was studied by filtration of humic acid (HA) solution and the results showed that HA rejection reached a peak of 96.88% for 0.3 wt. % PVC/MWCNT-COOH nanocomposite membrane. Finally, it was found that the antifouling properties of the membranes increased with increasing nanotube content, especially COOH-MWCNT.
کلیدواژه ها:
نویسندگان
Sepideh Masoumi Khosroshahi
Membrane Technology Research Center, Sahand University of Technology, Tabriz, Iran.
Alireza Miroliaei
Department of Chemical Engineering, University of Mohaghegh Ardabili, Ardabil, Iran.
Younes Jafarzadeh
Faculty of Chemical Engineering, Sahand University of Technology, Tabriz, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :