Evaluation and modification of copper mold wear properties in continuous steel casting processes with HVOF method
سال انتشار: 1397
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 367
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CARSE03_199
تاریخ نمایه سازی: 18 خرداد 1398
چکیده مقاله:
Usual techniques such as PVD and CVD unused for coating modification of copper mold due to their size, and to increase their wear resistance and lifetime, conventional hard chromium plating is used. The substitution of this technique with safer and more efficient ways has been recently studied and performed due to environmental pollution and restrictions for using Cr(VI) compounds, which are known to be carcinogenic. The aim of this research is to increase the life time of Dies by replacing Hard chromium with Thermal Spraying process. In order to this replacement, HVOF Thermal Spraying and 75Cr3C2-25NiCr cermet were selected as coating process and material respectively. Also, the Thermal Spray process was optimized by using The S/N ratio analysis approach and selecting four Kerosene Flow Rate (KFR), Feed Rate (FR), Spray Distance (SD) and Substrate Surface Roughness (SSR) parameters. Pin and Disc wear tester was used to compare wear rat e of these coatings. The results showed significant decrease of wear rate on the thermally sprayed samples. The results Also showed a desirable improvement of wear rate by optimizing parameters. Eventually, it is expected that the life time of dies should increase a lot. Keywords: die, hard chromium, HVOF Thermal Spraying, optimization, wear.
کلیدواژه ها:
نویسندگان
Hooman Pashaie Marandi
Master Student of Materials Science Engineering, Department of Materials & Metallurgy, Neyshabur Branch, Islamic Azad University, Neyshabur, Iran
H.R Emamian
Assistances Professor, Department of Materials & Metallurgy, Neyshabur Branch, Islamic Azad University, Neyshabur, Iran