Application of industrial immobilized TiO2 nanoparticles for photocatalytic treatment of dye solution in rectangular photoreactor
محل انتشار: سومین کنفرانس نانوساختارها
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,196
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CNS03_128
تاریخ نمایه سازی: 21 دی 1388
چکیده مقاله:
Photocatalytic decolorization of a dye solution containing C. I. Basic Blue 3 (BB3) was studied in the presence of industrial immobilized TiO2 nanoparticles irradiated by UV-C light. The investigated photocatalyst was industrial Millennium PC-500 (crystallites mean size 5-10 nm) immobilized on non-woven paper (Ahlstrom Research & Services). SEM images and X-ray analyses of the immobilized TiO2nanoparticles showed that it could be regenerated and used for several times. All the experiments were performed in a rectangular photochemical reactor equipped with a 30 W UV lamp emitted around 254 nm. Results showed that photocatalytic decolorization efficiency was small when the photolysis was carried out in the absence of immobilized TiO2 nanoparticles and it was also negligible in the absence of UV light. The effect of BB3 concentration was also examined. Results indicated that photocatalytic decolorization efficiency decreased with increasing the initial concentration of the dye. Photocatalytic decolorization process was explained in terms of the Langmuir-Hinshelwood kinetic model. The values of the adsorption equilibrium
constant, K, and the second order kinetic rate constant, k, were 0.0797 ppm-1 and 0.4202 ppm min-1 respectively.
کلیدواژه ها:
نویسندگان
A.R Khataee
Department of Applied Chemistry, Faculty of Chemistry, University of Tabriz, Tabriz, Iran
M Fathinia
Department of Applied Chemistry, Faculty of Chemistry, University of Tabriz
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :