Pervaporation performance of PDMS/PVDF/Polyester multilayer membrane in ethanol/water separation

سال انتشار: 1397
کد COI مقاله: ICESIT01_199
زبان مقاله: انگلیسیمشاهده این مقاله: 236
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
محتوای کامل این مقاله با فرمت WORD هم قابل دریافت می باشد.

خرید و دانلود فایل مقاله

با استفاده از پرداخت اینترنتی بسیار سریع و ساده می توانید اصل این مقاله را که دارای 9 صفحه است به صورت فایل PDF و یا WORD در اختیار داشته باشید.
آدرس ایمیل خود را در کادر زیر وارد نمایید:

مشخصات نویسندگان مقاله Pervaporation performance of PDMS/PVDF/Polyester multilayer membrane in ethanol/water separation

Shiva Shafiee - Separation Processes Research Group (SPRG), Department of Engineering, University of Kashan, Kashan, Iran
Mohammad Paki - Separation Processes Research Group (SPRG), Department of Engineering, University of Kashan, Kashan, Iran
Morteza Asghari - Associate Professor of Chemical Engineering, Separation Processes Research Group (SPRG), Department of Engineering, University of Kashan, Kashan, Iran

چکیده مقاله:

With the decrement of fossil fuels, the increment of oil prices and environmental requirements, there is an increasing need for the development of new energy sources, especially renewable energies such as ethanol. Membrane technology is one of the most effective, attractive and energy saving separation processes that is flourished over the world recently. Pervaporation (PV) is a membrane-based process which is used to separate the components of a liquid mixture. Polydimethylsiloxane (PDMS) membrane has attracted increasing attention due to its potential application in the separation of organic–organic liquid mixtures and removing volatile organic compounds from water and soil. However, the selectivity of neat PDMS membrane reported in papers is very low. Much effort has been expended to improve the overall PV performance of PDMS membranes due to its low-cost and easiness to handle, but there was no development in selectivity or permeation flux of neat PDMS membranes. Since Polyvinylidene fluoride (PVDF) is a porous membrane, dilute PDMS homogeneous solution is liable to plugging in the pores of PVDF membrane surface and may lead to the notable increase in permeation resistance across the interface of PVDF and PDMS for small molecules. In this paper, a multi-layer PDMS/PVDF composite membrane with an alternative configuration was prepared and subsequently applied in ethanol recovery from an ethanol-water mixture by PV process. The porous PVDF support layer was obtained by coating on the PET with phase inversion method. The selective layer (PDMS) was coated on the surface of PVDF porous substrate. The multi-layer composite membrane had the effective area of about 20 cm2 and the PET/PVDF/PDMS layers had the thickness of about 85/35/10 µm respectively. Atomic force microscopy (AFM) and Fourier transform infrared (FTIR) spectroscopy was performed on PDMS layer and x-ray diffraction (XRD) on multilayer membrane. The effect of feed temperature and feed ethanol concentration on the pervaporative properties of PDMS/PVDF composite membrane were investigated and the results were compared with the neat PDMS membrane. PV tests were performed in different temperatures(30,45,60,75) and various feed ethanol concentrations(5,10,15,20). Each experiment was performed three times and the average value was considered. It was found that, the total flux of the composite membrane increases with the increment of feed temperature, whereas the separation factor decreased. Experimental results showed that the membrane synthesized in this study had better separation factors at low ethanol concentrations in the feed and also in low temperatures. Maximum separation factor about 32 was obtained at 30⁰C and 5 wt% of ethanol concentration in the feed. In addition, the maximum flux was obtained at 75⁰ C and 15 wt%. The optimum conditions of selectivity and flux was tested on single layer PDMS membrane. Less separation factor and flux was obtained in the similar condition which indicates better efficiency of the multilayer membrane.

کلیدواژه ها:

Ethanol-water separation, Multilayer membrane, Pervaporation, PDMS/PVDF/Polyester membrane

کد مقاله/لینک ثابت به این مقاله

کد یکتای اختصاصی (COI) این مقاله در پایگاه سیویلیکا ICESIT01_199 میباشد و برای لینک دهی به این مقاله می توانید از لینک زیر استفاده نمایید. این لینک همیشه ثابت است و به عنوان سند ثبت مقاله در مرجع سیویلیکا مورد استفاده قرار میگیرد:

https://civilica.com/doc/836699/

نحوه استناد به مقاله:

در صورتی که می خواهید در اثر پژوهشی خود به این مقاله ارجاع دهید، به سادگی می توانید از عبارت زیر در بخش منابع و مراجع استفاده نمایید:
Shafiee, Shiva and Paki, Mohammad and Asghari, Morteza,1397,Pervaporation performance of PDMS/PVDF/Polyester multilayer membrane in ethanol/water separation,International Congress and Exhibition of Sciences and Innovative Technologies ,Babol,https://civilica.com/doc/836699

در داخل متن نیز هر جا که به عبارت و یا دستاوردی از این مقاله اشاره شود پس از ذکر مطلب، در داخل پارانتز، مشخصات زیر نوشته می شود.
برای بار اول: (1397, Shafiee, Shiva؛ Mohammad Paki and Morteza Asghari)
برای بار دوم به بعد: (1397, Shafiee؛ Paki and Asghari)
برای آشنایی کامل با نحوه مرجع نویسی لطفا بخش راهنمای سیویلیکا (مرجع دهی) را ملاحظه نمایید.

مدیریت اطلاعات پژوهشی

صدور گواهی نمایه سازی | گزارش اشکال مقاله | من نویسنده این مقاله هستم

اطلاعات استنادی این مقاله را به نرم افزارهای مدیریت اطلاعات علمی و استنادی ارسال نمایید و در تحقیقات خود از آن استفاده نمایید.

علم سنجی و رتبه بندی مقاله

مشخصات مرکز تولید کننده این مقاله به صورت زیر است:
نوع مرکز: دانشگاه دولتی
تعداد مقالات: 5,873
در بخش علم سنجی پایگاه سیویلیکا می توانید رتبه بندی علمی مراکز دانشگاهی و پژوهشی کشور را بر اساس آمار مقالات نمایه شده مشاهده نمایید.

مقالات پیشنهادی مرتبط

مقالات مرتبط جدید

به اشتراک گذاری این صفحه

اطلاعات بیشتر درباره COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.

پشتیبانی