Influence of Impregnation Ratio on the Properties of Activated Carbon Prepared via ZnCl2 Activation
محل انتشار: ششمین کنگره بین المللی مهندسی شیمی
سال انتشار: 1388
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 2,655
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC06_595
تاریخ نمایه سازی: 1 مهر 1388
چکیده مقاله:
In this study, an activated carbon with high surface area was prepared from walnut shell by chemical activation using ZnCl2. Impregnation ratios of activating agent to dry precursor (wt/wt) were selected in the range of 0.5–2.0. The influences of impregnation ratio on the characterization of the activated carbon were investigated by SEM (scanning electron microscopy), FTIR (transmittance Fourier infrared spectroscopy) and XRD (X-ray diffraction) analysis. The SEM analysis shows there is a good and successful pore development in the activated carbon obtained with increasingimpregnation ratios. X-ray diffraction patterns showed broad peaks, that suggesting either that structure is amorphous or that the particles are really too small particles or too low concentration of adsorbed material to diffract. The surface areas of the activated carbons increased with increasing impregnation ratios and the maximum value of the BET surface area can reach 2643 m2/g at impregnation ratio 2:1. The FTIR analysis showed that at high impregnation ratios the formation of aromatic rings was favored, while the formation of acidic surface groups was favored at lower impregnation ratios. Efficiency of activated carbon production has shown an optimum impregnation ratio of 2:1.
کلیدواژه ها:
نویسندگان
Leila Karimnezhad
Chemical Engineering Department, Sahand University of Technology, P.O.Box ۵۱۳۳۵-۱۹۹۶, Sahand New Town, Tabriz, Iran.
Mohammad Haghighi
Environmental Engineering Research Center (EERC), Sahand University of Technology, P.O.Box ۵۱۳۳۵-۱۹۹۶, Sahand New Town, Tabriz, Iran.
Esmaeil Fatehifar
Environmental Engineering Research Center (EERC), Sahand University of Technology, P.O.Box ۵۱۳۳۵-۱۹۹۶, Sahand New Town, Tabriz, Iran.
Nader Rahemi
Reactor and Catalysis Research Center (RCRC), Sahand University of Technology, P.O.Box ۵۱۳۳۵-۱۹۹۶, Sahand New Town, Tabriz, Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :