The Empirical Comparison between Solutionized-compressed and Aged-compressed of a Mg Alloy Regarding Microstructure

سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 305

فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

ICCEAS01_040

تاریخ نمایه سازی: 26 مرداد 1397

چکیده مقاله:

The present research investigated ageing treatment on dynamic recrystallization and texture in Mg-Zn alloy by optical microscopy (OM), transmission electron microscopy (TEM) and electron backscattered diffraction (EBSD). Mg-6 wt.%Zn alloys were firstly solution and ageing treatment, and then the solutionized and peak-aged alloys were compressed at elevated temperature. The microstructure and texture were systematically investigated. Optical microstructure showed that ageing treatment prohibited dynamic recrystallization during deformation, which was because the precipitates inhibited dislocation movement and restricted the formation of deformation bands. The DRXed region and deformed region both contained typical basal texture with basal planes oriented perpendicular compression direction, but the recrystallized region showed a much weaker texture. The peak-aged alloy containing rod-shaped precipitates exhibited stronger texture intensity after dynamic recyrallization compared with the as-solutionized alloy, which was because the precipitates in the peak-aged alloy inhibited the lattice rotation of the newly formed DRXed grains or affected the microstructural evolution.

کلیدواژه ها:

Ageing treatment ، Optical Microscopy(OM) ، Transmission Electron Microscopy (TEM) ، Electron Backscattered Diffraction (EBSD) ، Precipitates