The Effect of Heat Treatment on Weld Strength of Al- Steel Joints with Different Thicknesses
سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 433
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IMES11_101
تاریخ نمایه سازی: 7 اسفند 1396
چکیده مقاله:
In the present study the effect of heat treatment on bond strength and intermetallic formation in dissimilar Aluminum-steel joints was investigated. Whereas the softer metal (Aluminum) was thinner, all samples were fractured from weld zone. Therefore, it was possible to evaluate the bond strength of the welds even when the bond strength of the weld exceeded the base material. It was observed that as welded sheets have the bond strength equivalent to the base material and the toughness were so low. After heat treatment for 1 hour, the bond strength and elongation increased considerably but thereafter increased time of heat treatment led to degradation of weld strength and elongation.
کلیدواژه ها:
نویسندگان
R. Beygi
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak
S. Ahmadi
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak
M. Zarezadeh Mehrizi
Department of Materials Science and Engineering, Faculty of Engineering, Arak University, Arak
M. Rezvanyvardom
Department of Electrical Engineering, Faculty of Engineering, Arak University, Arak, Iran.