Thin film complex membranes for forward osmosis application with the result of SiO2 nanoparticles on biography and performance
سال انتشار: 1396
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 629
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
CCES03_030
تاریخ نمایه سازی: 7 اسفند 1396
چکیده مقاله:
This paper presents polyamide nano-composite membrane containing silica nanoparticles (TFN) synthesized via in situ interfacial polymerization for the forward osmosis (FO) application. Different concentrations of silica nanoparticles (0.02, 0.06 and 0.2%w/v) were added to the aqueous solution as additive to improve the FOmembrane performance. The prepared membranes were characterized by ATR-FTIR, SEM, AFM and hydrophilicity measurement. The structure of nanocomposite layer synthesized by interfacial polymerization was characterized by FTIR spectroscopy. The FTIR peaks confirmed the presence of polyamide layer with SiO2 nanoparticles. The morphological studies showed that the SiO2 nanoparticleswere effectively attached to the FO membrane surface. The contact angle measurements showed that the hydrophilicity of FO membranes was improved with increasing SiO2 in the aqueous solution. The FO performance was measured using 10mMNaCl solution as feed solution and 3 M NaCl solution as draw solution in both orientations. The TFN membranes showed higher water permeability and better salt rejection in the range of 0.02–0.2wt.% silica loading in comparisonwith the TFC membrane. The water flux of the TFN membrane reached to a maximum of 36±2 L/m2 h which is nearly 2 times as high as that of the TFC membrane and it was found that the membrane modified with 0.06 w/v.% silica nanoparticles showed the highest salt rejection (92 ± 4%).
کلیدواژه ها:
نویسندگان
Sajad Alimohammadi
Azad University of boroujerd
Mohamad Fallahiyekta
Azad University of boroujerd
Arsalan Parvardeh
Azad University of boroujerd