For investigating the properties of poly (lactic acid) (PLA)/poly(έ-caprolactone)(PCL) blends in this study PLA/PCL blends were prepared with 7, 15 and 30 % PCL via melt mixing method in the internal mixer (Brabender). The morphology of PLA/PCL blends was observed by scanning electron microscopy (SEM) and the effect of PCL content on the mechanical properties was studied. The results of SEM showed that the PLA/PCL blends are immiscible and phase-separated and that the size of dispersed phase (PCL) increases with addition PCL content. The mechanical properties as modulus and tensile strength reduce while the elongation at break and toughness increased by adding PCL to PLA matrix and the brittleness PLA improves.

نویسندگان

Zahra Zamani

Department of Polymer Engineering, Faculty of Engineering, Qom University of Technology, P.O. Box: ۳۷۱۹۵-۱۵۱۹, Qom, Iran.

Mohsen Mohammadi

Department of Polymer Engineering, Faculty of Engineering, Qom University of Technology, P.O. Box: ۳۷۱۹۵-۱۵۱۹, Qom, Iran.

Hamed Azizi

Department of Plastics Engineering, Faculty of Polymer Processing, Iran Polymer and Petrochemical Institute, P.O. Box: ۱۴۹۶۵-۱۱۵, Tehran, Iran.

Jafar Khademzadeh Yeganeh

Department of Polymer Engineering, Faculty of Engineering, Qom University of Technology,P.O. Box: ۳۷۱۹۵-۱۵۱۹, Qom, Iran.