Investigation on the Effects of Magnetic Field on Bromide-Induced Pitting of Commercially Pure Titanium
محل انتشار: دهمین کنگره ملی خوردگی ایران
سال انتشار: 1386
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,472
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
INCC10_033
تاریخ نمایه سازی: 4 اسفند 1387
چکیده مقاله:
In chloride salt solutions, titanium alloys exhibit reasonably high pitting potentials as high as +10 V (vs. AglAgCI) at room temperature. On the other hand. anodic pitting potentials are significantly lower in bromide solutions. In this study, pitting corrosion of commercially pure titanium in aqueous NaBr solution of 0.1 M concentration at room temperature was studied and the effect of an external magnetic field oriented both parallel and perpendicular to electrode surface was investigated. Cyclic potentiodynamic and potentiostatic polarization tests were carried out. Anodic breakdown potential of+1.4 V (vs, AglAgCl) obtained in the absence ofmagnetic field, decreasing to +1.1 V in the presence of a 0.05 T parallel magnetic field. The perpendicular magnetic field actually did not affect the breakdownpotential. Applying of an external magnetic field, independent of its orientation, shifted the repassivation potential 100 mV in the positive direction. SEM microscopy observations of sample surfaces indicated that applying of magnetic field results in some variations in the pit shapes and their sizes.
کلیدواژه ها:
نویسندگان
H Fattahi
MSc. Student, Department ofMaterials Science andEngineering, Shiraz University,
M.H shariat
Professor. Department ofMaterials Science and Engineering, Shiraz University.