SYNTHESS OF TB2-AL2O3 NANOSTRUCTURE THIROUGH MECHANOCHEMICAL PROCESS

سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 289

فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

UFGNSM03_245

تاریخ نمایه سازی: 10 تیر 1396

چکیده مقاله:

The nanostructure composites of TiE2 such as TiB2-Al2O3 are useful in variety of applications such as cutting tools, wear-resistant substrates, and lightweight armor. On the other hand, recently, mechanical activation and mechanical milling have been extensively implemented for synthesizing nanostructure composite powders and advanced materials. In this present research, TiB2-Al2O3 nanostructure composite was produced using mixtures of titanium dioxide, boric acid and pure aluminum as raw materials through mechanochemical process. The milled powders were studied by XRD, SEM analytical techniques. According to the XRD patterns, Synthesis of TiB2-Al2O3 nanostructure was not occurred until 40 h milling process. XRD analyses exhibited that the TiB2-Al2O3 nanostructure was formed after this milling time. The results indicate that increasing milling time up to 80 h had no significant effect other than refining the crystallite sizes of the components specially TiB2.

نویسندگان

BEHZAD AMINIKLA

Materials and Energy Research Center (MERC) Alvand street, Tehran, Iran. Po. Box ۱۴۱۵۵-۴۷۷۷