FACLE SYNTHESS OF CERIUMOXDENANOSTRUCTURE MATERALS VIA MOLTENSALTSYNTHESIS (MSS) METHOD

In this study, Ceria nano 1D fluorite cubic nanostructures with ~60 nmin diameter and 280 nm in length were prepared by novel and very facile low temperature molten hydroxide synthesis method after only 0.5 h of reaction time without further heat treatment. The cerium hexachloride reacted with molten KOH-NaOH above eutectic temperature to synthesis the ceria nanostructures. Brunauer, Emmett and Teller (BET), X-ray diffraction, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were employed to analyse the phase structure, morphological study and surface area determinations, respectively. It is observed that nano particles were obtained at the first reaction time while rod formation appeared at this stage of reaction and grew to larger scale by selfassembly processC5um). Diffracted peak shifts slowly with further reaction time which is attributed to the larger lattice parameter

کلیدواژه ها:

Ceria ، nano structure ، synthesis ، moltenhydroxide