LOW TEMPERATURE MOLTEN SALT SYNTHESS OF NANOCRYSTALLINE MGALO, SPINEL POWDER USING NACL SALT MEDIA
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 355
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
UFGNSM03_069
تاریخ نمایه سازی: 10 تیر 1396
چکیده مقاله:
MgAl2O4 (MA) spinel nano powder was synthesized using a molten salt technique, by heating stochiometric composition of MgO and AlOOH. NaCl salt was used as reactor media for MA spinel formation. Reactants and molten salt mixtures were fired in an alumina crucible for 3 h at temperature ranges from 850 °C to 1000 °C. The synthesis temperature was decreased from 1300 C required by the conventional solid-solid reaction process to 850 C for molten salt approach. The synthesized powders were characterized by X-ray diffraction pattern OXRD), scaning electron microscopy (SEM) and Brunauer-Emmett–Teller technique (BET). XRD revealed complete formation of MA without remaining of any secondary phase for synthesized powder fired at 850 °C for 3 h. Moreover, electron microscopy illustrated that the MA morphology and size was the same as the nano boehmite morphology which confirmed the existence of a template process mechanism during the molten salt synthesis. In addition, high surface area for nano MA powders was achieved in this method.
کلیدواژه ها:
نویسندگان
Y. SAFAE-NAEN
School of Metallurgy and Materials Engineering, Iran University of Science and Technology Tehran, Iran
M. AMINZARE
School of Metallurgy and Materials Engineering, Iran University of Science and Technology Tehran, Iran
F. GOLESTANI-FARD
School of Metallurgy and Materials Engineering, Iran University of Science and Technology Tehran, Iran