PREPARATION OF γ-ALUMINA AS A SUITABLE SUPPORT FOR HDS CATALYST
محل انتشار: دوازدهمین کنگره ملی مهندسی شیمی ایران
سال انتشار: 1387
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,742
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NICEC12_097
تاریخ نمایه سازی: 30 شهریور 1387
چکیده مقاله:
In this article γ-Alumina as a favorable hydrodesulphurization (HDS) catalyst support was experimentally synthesized. Aluminum sulfate and sodium aluminate were used as raw materials whose aqueous solutions were reacted to produce aluminum oxide gel. The resulting gel is phase-separated, filtrated, extruded and finally dried to form solid γ-Alumina. In order to measure the surface area of produced sample, liquid nitrogen adsorption/desorption isotherms were achieved and introduced in the well-known equation of BET. The results show that the surface area of produced support in comparison with the similar commercial types was in the moderate range.
نویسندگان
S Azizi
Islamic Azad University, Mahshahr branch
S. Fatemi
۲Faculty of Engineering, University of Tehran
S.M Peyghambarzadeh
Islamic Azad University, Mahshahr branch
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :