Boundary Element Method Predictions Analysis of Galvanic Corrosion of Zinc/Steel Interface under a Thin Layer of NaCl Solution
سال انتشار: 1387
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 3,284
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
SCMEMI08_011
تاریخ نمایه سازی: 5 مرداد 1387
چکیده مقاله:
This research investigated the galvanic corrosion of a Zinc/Steel interface under a thin layer of NaCl solution by Boundary Element Method (BEM) model. It was assumed that both oxygen reduction and iron oxidation could occur on the Fe surface, while only zinc oxidation occurred on the Zn surface. The boundary condition, required as an input into the BEM model, needs to be a polarization curve that accurately reflects the corrosion process. Provided that the polarization curve does reflect steady state, the BEM model is expected to be able to reflect steady state galvanic corrosion. Using data obtained from Boundary Element Method the effect of electrolyte thickness and conductivity on galvanic corrosion of the Zn coupled to steel was investigated.
کلیدواژه ها:
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :