Dynamic Recrystallization Kinetics of AISI 403 Stainless Steel Using Hot Compression Test

سال انتشار: 1393
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 419

فایل این مقاله در 12 صفحه با فرمت PDF قابل دریافت می باشد

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

JR_IJMF-1-2_004

تاریخ نمایه سازی: 8 دی 1395

چکیده مقاله:

In this work dynamic recrystallization behavior of AISI 403 martensitic stainless steelwas studied using hot compression tests over temperature range of 900°C -1200°C and strain raterange of 0.001 s-1-1 s-1. The obtained flow curves showed that the hot compression behavior of thealloy is controlled by dynamic recrystallization. The flow stress and strain corresponding to thecritical, peak and onset of steady state region were related to the Zener-Hollomon parameter usingsimple power equations. The variation of dynamic recrystallization fraction with strain showedthat restoration kinetics is enhanced with increasing the temperature and decreasing the strain rate.The development of DRX was modeled using Avrami Kinetics equation. The equations proposedby Baragar and Cingara-McQueen were used to develop a new model capable of predicting theflow curves up to the onset of steady state flow region. This softening work is mainly controlledby the phenomenon of dynamic recrystallization.

نویسندگان

E Kevanlo

Department of Materials and Polymer Engineering, Hakim Sabzevari University, Sabzevar, Iran

G.R Ebrahimi

Department of Materials and Polymer Engineering, Hakim Sabzevari University, Sabzevar, Iran

S.A.A Sani

Department of Materials Science and Engineering, Iran University of Sience and Technology, Tehran, Iran

A Momeni

Department of Materials Science and Engineering, Hamedan University of Technology, Hamedan, Iran