Application of plasma technology to improve the mechanical properties of carbon fiber composite
محل انتشار: کنفرانس بین المللی علوم مکانیک و صنعت
سال انتشار: 1394
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 588
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICMST01_010
تاریخ نمایه سازی: 26 شهریور 1395
چکیده مقاله:
The objectives of this research were to assess the effect of oxygen plasma treatment on properties of carbon fibers and interfacial adhesion behavior between the carbon fibers and epoxy resin. The adhesion between the carbon fiber and matrix was examined by interlaminar shear strength (ILSS). Furthermore, carbon fibers were characterized by Raman spectroscopy analysis and tensile strength test. It was observed that the composites produced from plasma treated carbon fiber have higher ILSS compared with untreated fibers, However long exposure times could partly damage the surface of carbon fibers and decrease the tensile strength of filaments and ILSS of treated fiber composites.
کلیدواژه ها:
نویسندگان
Meysam Baghery Borooj
Textile Engineering Department, Amirkabir University of Technology, Tehran, Iran
Ahmad Mousavi Shoushtari
Textile Engineering Department, Amirkabir University of Technology, Tehran, Iran
Aminoddin Haji
Textile Engineering Department, Birjand Branch, Islamic Azad University, Birjand, Iran
Ehsanollah Nosratian Sabet
Textile Engineering Department, Amirkabir University of Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :