Preparation of mesoporous silica spheres with high surface area
سال انتشار: 1394
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 507
فایل این مقاله در 5 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ITCC02_246
تاریخ نمایه سازی: 21 شهریور 1395
چکیده مقاله:
Mesoporous materials have attracted much attention not only due to porous features for adsorbents and catalysts but also due to electronic, magnetic, and optical properties for advanced devices. Silica spheres with mesoporous structures have potential applications in drug storage and release, confined-space catalysis, separation and energy storage. In this study, mesoporous silica spheres were synthesized by a sol–gel/emulsion approach, in which cetyltrimethylammonium bromide (CTAB) surfactant was employed to stabilize and direct the hydrolysis of oil droplets of tetraethoxysilane (TEOS). In this method, the mixture of water and ethanol was used instead of water in the conventional oil-in-water emulsion system to improve the stability of the oil droplets, thus allowing the preparation of silica spheres with improved size distribution. The diameters of the silica spheres were in the range from 300 to 400 nm. BET surface areas of the silica spheres were determined to be high up to 1208 m2g-1 and their pore size were around 2.66 nm as determined by BJH method.
کلیدواژه ها:
نویسندگان
Vajihe Khani
Department of Materials Science and Engineering, Tarbiat Modares University
Parvin Alizadeh
Department of Materials Science and Engineering, Tarbiat Modares University
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :