EXTRACTION OF SILICA FROM BAGASSE AND POST-SYNTHETIC OF HEIRARCHICAL ZSM-5 ZEOLITE FROM THAT AND THEIR CHARACTERIZATION
سال انتشار: 1395
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 923
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
TCPCO03_027
تاریخ نمایه سازی: 16 شهریور 1395
چکیده مقاله:
Pure silica powder was extracted from bagasse. After that, ZSM-5 zeolite was synthesized by conventional hydrothermal method using this extracted silica source. Then, post-synthetic modification of ZSM-5 zeolite (Si/Al=35), was investigated by desilication using alkaline treatment (NaOH solution). Extracted silica from bagasse was characterized by X-ray fluorescence spectrometry (XRF), (Furrier Transform Infra-Red) FT-IR spectra and X-ray Diffraction (XRD). Also, ZSM-5 synthesized before and after alkaline treatment was characterized and compared with each other. Characterization of these zeolites was performed by field-emission scanning electron microscope (FESEM) and X-ray Diffraction (XRD). Surface area of ZSM-5 before and after desilication was 352 and 401 m2 g-1.
کلیدواژه ها:
نویسندگان
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :