Synthesis of nano zirconia powders by sucrose as a chelating agent and template material and their applications for CH4/CO2 reforming
محل انتشار: پنجمین کنگره بین المللی مهندسی شیمی
سال انتشار: 1386
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,484
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
ICHEC05_475
تاریخ نمایه سازی: 7 بهمن 1386
چکیده مقاله:
Nanocrystalline of zirconia and zirconia doped with yttrium, cerium and lanthanum oxides have been prepared from an aqueous solution of metal precursors and sucrose. Metal solution forms the precursor material once it is completely dehydrated. Calcination ions-sucrose of the dehydrated precursors results in the formation of nanocrystalline of zirconia powders. The resultant powders were characterized by TGA/DTA, XRD, BET and Hg porosimetery techniques. XRD and BET analysis showed that the addition of dopants increased the thermal stability of the powders and stabilized the tetragonal phase at room temperature. The catalytic activity of nickel catalysts supported on the synthesized powders was studied in methane reforming with carbon dioxide and the obtained results showed that the addition of dopants improved the activity and stability of catalysts, which the promotional effects of these dopants may stem from their abilities to increase the thermal stability of the support.
کلیدواژه ها:
نویسندگان
Rezaei
Chemical Engineering Department, Faculty of Engineering, University of Kashan, Kashan, Iran, State Key Laboratory for Heavy Oil Processing, Key Laboratory of Catalysis, CNPC, China University of Petroleum, Dongying ۲۵۷۰۶۱, China
Alavi
Chemical Engineering Department, Iran University of Science and Technology, Tehran, Iran
Sahebdelfar
Petrochemical Research & Technology Company (NPC-RT), Tehran, Iran
Zi-Feng Yan
State Key Laboratory for Heavy Oil Processing, Key Laboratory of Catalysis, CNPC, China University of Petroleum, Dongying ۲۵۷۰۶۱, China
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :