Introducing a Novel Structure for Improving SnO2 Thin Filmfor Propane Detection
سال انتشار: 1393
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,229
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
NANOCONF01_023
تاریخ نمایه سازی: 7 آبان 1393
چکیده مقاله:
A new double layers structure was proposed to improve sensitivity of tinoxide thin films in propane atmosphere. Three different thickness (200 nm,250 nm and 300 nm) were deposited on glass substrates (~ 20 mm 25mm 2 mm) using electron beam evaporation and annealed at fourdifferent temperatures. Propane (C3H8) sensing of all prepared samplesover a temperature range of 100°C to 400°C was investigated to achievethe optimum condition for gas sensing. The structure with 250 nmthickness which was annealed at 400°C showed the highest sensitivity of26% at an operating temperature of 315°C. The second layer with 60 nmthickness was deposited on this film to make 250/60 nm structure. Thisnew structure enhanced the sensitivity of the sample to 68% at a loweroptimum working temperature of 280°C. The morphology of the sampleswas characterized by atomic force microscopy (AFM) image.
کلیدواژه ها:
نویسندگان
D. Meshgi
School of Electrical & Computer Engineering, Shiraz University, Shiraz, Iran
M. H. Sheikhi
Nanotechnology Research Institute, Shiraz University, Shiraz, Iran
Z. Karami Horastani
Department of Electrical & Computer Engineering, Isfahan University of Technology, Isfahan,Iran
S. Zeinali
Department of nanochemical engineering, Shiraz University, Shiraz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :