Investigating the Effect of Modifier Chain Length on Insulation Properties of Polysulfide Modified Epoxy Resin

Polysulfide resins,with trade name of  G۴ and G۱۱۲, with short and long chain lengths respectively, were used as reactive modifiers to toughen epoxy resin. The effects of molecular weights of G۴ and G۱۱۲ on impact resistance, dielectric constant, thermal conductivity as well as decomposition  heat and adhesion properties of toughened epoxy were investigated. The impact strength and the dielectric constant of epoxy resin were enhanced by increasing of polysulfide so that the effect of the G۱۱۲ is higher than the G۴. For the same weight percent of G۴ and G۱۱۲, the G۱۱۲ modified epoxy resin has lower Cure enthalpy than the G۴ modified epoxy resin. Addition of modifier with long chain up to ۱۰ weight percent was also leaded to higher bond strength with aluminum sheets. also, It is observed that the thermal conductivity of epoxy decreasing with incresing modifier chain length.

کلیدواژه ها:

epoxy ، Polysulfide ، Insulation properties