EVALUATION AND INVESTIGATION OF MAIN FAILURES IN SOUR GAS ENVIRONMENT
سال انتشار: 1385
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,593
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
SCCE06_091
تاریخ نمایه سازی: 18 دی 1385
چکیده مقاله:
Large amount of the natural gas produced in Iran is sour. The presence of hydrogen sulfide and carbon dioxide in
hydrocarbon reservoirs can create significant materials problems.
In this paper tried to evaluate and investigate the failures that produced in the sour gas environment in oil and gas
industry and the parameters that affect these failures. Materials degradation can take many forms, including sulfide-
stress cracking, Hydrogen-induced cracking, Stress-corrosion cracking and weight- loss corrosion. Each of these
must be understood if appropriate measures are to be taken to minimize its effect in field operations.
Parameters such as H2S concentration, PH, temperature, strength level, cold work, on the first type corrosion (SSC),
the amount of total stress and shape of defects on second type corrosion (HIC) can have basic effects. Concentration
of chloride and H2S, and temperature also can cause SCC to decrease or increase.
It is clear that safety issues are of primary importance in selecting materials for sour service. Even a small leakage of
H2S into the environment can cause extreme danger to the surrounding area. Exposure to H2S can produce adverse
effects on human health and behavior, depending on concentration and length of exposure. It could be controlled by
appropriate choose of material (material selection) or by use suitable inhibitors. Equipment design is often very
important in obtaining resistance to SSC.
کلیدواژه ها:
sour gas ، sulfide-stress cracking ، Hydrogen-induced cracking ، Stress-corrosion cracking and weight-loss corrosion