An effective survey on the behavior of LiTaO(3) nanopowder

سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 825

متن کامل این مقاله منتشر نشده است و فقط به صورت چکیده یا چکیده مبسوط در پایگاه موجود می باشد.
توضیح: معمولا کلیه مقالاتی که کمتر از ۵ صفحه باشند در پایگاه سیویلیکا اصل مقاله (فول تکست) محسوب نمی شوند و فقط کاربران عضو بدون کسر اعتبار می توانند فایل آنها را دریافت نمایند.

استخراج به نرم افزارهای پژوهشی:

لینک ثابت به این مقاله:

شناسه ملی سند علمی:

IAUET01_059

تاریخ نمایه سازی: 9 تیر 1392

چکیده مقاله:

The Main aim of this work is establishing a simple and effective processing route for the preparation of LiTaO(3) nanopowder by combining conventional and well established ceramic processing techniques, such as the solid state synthesis of submicron sized powder and subsequent efficient milling to nano-range in an agitator bead mill. The influences of the milling time and different rotation speeds of the agitator shaft were followed by measurements of the particle size and size distribution and specific surface area. The optimization of the process resulted in a successful preparation of LiTaO(3) nanopowder. Furthermore, the nanopowder was isostatically pressed between 250 MPa and 740 MPa and its compaction-response diagram was constructed. In this research,We report the processing of LiTaO(3) nanopowder by combining the solid state synthesis and subsequent milling in the agitator bead mill. The effect of different rotation speeds of the agitator shaft on the comminution process was followed by laser granulometry. The morphology and specific surface area of the powders were investigated by scanning electron microscopy and the N(2) adsorption method, respectively. With the optimized milling parameters we obtained LiTaO(3) nanoparticles with an average size of 25 nm and a narrow particle size distribution. The result is comparable to other processing techniques, such as solution-based chemical routes or mechanochemical synthesis, however, the presented method does not require any complicated processing and it can be easily upscaled to yield large quantities of the LiTaO(3) nanopowder. Furthermore, the compaction behaviour of the obtained nanopowder was investigated, and a compaction-response diagram was constructed revealing good compactability of the powder. The green compacts, isostatically pressed at 740 MPa, had a relative density of 70 % and a narrow pore size distribution with an average pore radius of 4 nm.

نویسندگان

Kourosh Motevalli

Department of Applied Chemistry, Islamic Azad University, South Tehran Branch, Tehran, Iran

Zahra Yaghoubi

Faculty of Industrial Engineering, Islamic Azad University, South Tehran Branch, Tehran, Iran

مراجع و منابع این مقاله:

لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :
  • Ricketts, "Optimization of energy storage density in ceramic capacitors". Journal ...
  • (Pb, _ Sn)O Family of Ceramics" Journal of Applied Physics, ...
  • Zirconate". Physical Review, 1951, vol. 84, no. 3, p. 6, ...
  • Kri stallographie, 2011, vol. 226, no. 2, p. 163- 170.. ...
  • نمایش کامل مراجع