Investigation of microstructure and mechanical properties of hybrid composite of Aluminum/Alumina/Titanium carbide produced by rolling processes
محل انتشار: دومین کنفرانس بین المللی آلومینیوم
سال انتشار: 1391
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,470
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
IIAC02_046
تاریخ نمایه سازی: 12 اردیبهشت 1392
چکیده مقاله:
Accumulative roll bonding (ARB) is one of the severe plastic deformation processes that is used nowadays to produce metal matrix composites (MMCs) extensively. In this paper Al/Al2O3/TiC hybrid composite was produced using ARB and anodizing processes. The aim of the present work is to produce high strength Al/Al2O3/TiC hybrid composite with a different volume fraction of alumina and titanium carbide uniformly dispersed in aluminum matrix using the above processes. Alumina layer with different thickness was achieved with anodizing of aluminum at different times. Microstructure observations showed that by increasing the number of rolling cycles, distribution of reinforcement particles (Al2O3, TiC) in aluminum matrix became more uniform. Mechanical properties of hybrid composite were evaluated at different passes of ARB process. As strain was increased (with increasing the number of passes), mechanical properties of produced composite such as tensile strength were increased consequently. But ductility at first was decreased and then increased. It can also be seen that by increasing quantity of alumina and titanium carbide, tensile strength is improved.
کلیدواژه ها:
نویسندگان
Hajar Farajzadeh Dehkordi
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
Mohammad Reza Toroghinejad
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
Keyvan Raeissi
Department of Materials Engineering, Isfahan University of Technology, Isfahan ۸۴۱۵۶-۸۳۱۱۱, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :