A New Potential Contrast Agent for Magnetic Resonance Imaging: Iron Oxide-۴A Nanocomposite
محل انتشار: مجله فیزیک و مهندسی پزشکی، دوره: 9، شماره: 2
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 126
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JBPE-9-2_009
تاریخ نمایه سازی: 30 دی 1402
چکیده مقاله:
Background: Magnetic resonance imaging (MRI) contrast agents have an important role to differentiate healthy and diseased tissues. Access and design new contrast agents for the optimal use of MRI are necessary. This study aims to evaluate iron oxide–۴A nanocomposite ability to act as a magnetic resonance imaging contrast agent. Material and Methods: Iron oxide–۴A nanocomposite (F۴A) was synthesized. MTT assay was used to consider the nanocomposite safety for cell culture. The T۱ and T۲ relaxation times were measured using a ۱.۵ Tesla clinical MRI scanner. Then the corresponding relaxivities were determined.Results: The average particle diameter of the nanocomposite was ۵۰ to ۱۰۰ nm based on scanning electron microscope (SEM) image. A linear relationship between relaxation rates and the Fe concentration of the nanocomposite was obtained. The T۱ and T۲ relaxivities of the nanocomposite were calculated ۵.۴۱۳ and ۱۰۹۲.۱ mM-۱.s-۱, respectively which led to the T۲/T۱ relaxivity ratio of ۲۰۱.۷۵. Conclusion: The high T۲/T۱ relaxivity ratio of the iron oxide–۴A nanocomposite confirms it’s potential to act as a T۲ contrast agent.
کلیدواژه ها:
نویسندگان
L Zareei
Immunology Research Center, Tabriz University of Medical Sciences, Tabriz, Iran
B Divband
Department of Inorganic Chemistry, Faculty of Chemistry, University of Tabriz, C.P. ۵۱۶۶۴, Tabriz, Iran
A Mesbahi
Department of Medical Physics, Tabriz University of Medical Sciences, Tabriz, Iran
M Khatamian
Department of Inorganic Chemistry, Faculty of Chemistry, University of Tabriz, C.P. ۵۱۶۶۴, Tabriz, Iran
A Kiani
Department of MRI, Tabriz University of Medical Sciences, Tabriz, Iran
N Gharehaghaji
Department of Radiology, School of Paramedicine, Tabriz University of Medical Sciences, Tabriz, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :