Effect of aging temperature on structural evolution of HP-Nb heat resistant steel

In this study, the changes in microstructure of HP-Nb cast heat resistant steel after ۸ years of service at high temperatures were investigated. Study of microstructure using optical microscopy (OM) and scanning electron microscopy (SEM) equipped with an energy dispersive spectrometry (EDS) showed that the microstructure of this steel in as-cast condition includes an austenitic matrix, and that continuous eutectic-type precipitates in grain boundaries. These deposits include M۲۳C۶ chromium carbide and NbC. Aged sample microstructure at intermediate temperature (۷۰۰-۹۰۰ °C) consists of an austenitic matrix, M۲۳C۶ chromium carbides and blocky G-phase. The reason for this microstructure is the instability of NbC during aging at medium temperature ۷۰۰-۱۰۰۰ °C which, as a partially phase transformation, is transformed to G-phase. But in the samples aged at higher temperatures (۱۰۰۰-۱۱۰۰ °C), there are only two types of NbC and agglomerated M۲۳C۶ carbide precipitations, and the skeletal morphology of NbC carbides has become spherical.

کلیدواژه ها:

HP-Nb cast heat resistant steel ، Microstructure ، chromium carbide ، G-phase