The Effect of Flux type and Oxygen Blowing on Simultaneous Removal of Phosphorus and Sulfur from Molten Iron
سال انتشار: 1388
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 36
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-6-2_006
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
This research was conducted to study the effect of lime based Flux with the composition of CaO-۲۰%CaF۲-۸%FeO on simultaneous removal of phosphorus and Sulfur from hot metal. The effects of Na۲O and oxygen blowing were also studied. The experiments were performed using an induction furnace and hot metal produced in Isfahan Steel Company in the temperature range ۱۳۵۰-۱۴۵۰ ºC. The results showed that simultaneous removal of these elements was possible. It was also indicated that addition of Na۲CO۳ as the supplier of Na۲O caused a considerable improvement in the removal process. This was mainly because of an increase in slag basicity and CO۲ gas evolution. Oxygen blowing into the melt improved the phosphorus removal slightly. However, an increase in melt temperature resulted in some sulfur return from slag to hot metal. On the other hand, increase in melt oxygen potential due to oxygen blowing decreased desulfurization to some extent. According to the results obtained, ۳۵% and ۷۵% decrease in phosphorus and sulfur content of the melt was achieved respectively. The initial silicon content of hot metal was found to be an important parameter. The results showed that the hot metal silicon content should be reduced to less than ۰.۱۵% before phosphorus removal starts.
کلیدواژه ها:
نویسندگان
H. Abdeyazdan
Isfahan University of Technology, Isfahan, ۸۴۱۵۶۸۳۱۱۱,Iran
H. Edris
Isfahan University of Technology, Isfahan, ۸۴۱۵۶۸۳۱۱۱,Iran
M. Abbasi
Isfahan University of Technology, Isfahan, ۸۴۱۵۶۸۳۱۱۱,Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :