Investigating the contribution of wear caused by impact and abrasion in semi autogenous grinding mills
سال انتشار: 1401
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 81
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ISSIRAN-19-2_008
تاریخ نمایه سازی: 6 آبان 1402
چکیده مقاله:
Milling is one of the most important operational stages in steel and copper processing. Liners and lifters are used inside mill to extend their life and to enhance the grinding and crushing efficiency. The wear of lifters is influenced by a range of parameters such as: media charge level and mill speed. In this work, the researcher used a pilot mill of ۱m diameter and ۰.۵m length to investigate the influences of ball filling and the mill speed on the impact wear of lifters under wet condition. The contribution of impact wear and abrasive wear from the total wear was investigated with new mechanical test method. A copper ore smaller than one inch was used to prepare slurry at ۶۰% solids concentration of mass and slurry filling U=۱. The ball filling is ۱۰%, ۲۰% and ۳۰% of mill volume at different mill speeds from ۶۰% to ۱۰۰% of the critical speed. It was found that while there is an increase in ball filling the wear impact decreases. The wear rate was maximum when the mill speed varied between ۸۰% and ۹۰% of the critical speed. To find out the role of impact on the wear, a mechanism was devised and installed on the pilot mill to prevent the cascade motion.
کلیدواژه ها:
نویسندگان
Moslem Mohammadi Soleymani
Department of Mechanical Engineering, Payame Noor University (PNU), P.O. Box. ۱۹۳۹۵-۳۶۹۷, Tehran, Iran
Mehdi Bahiraie
Department of Mechanical Engineering, University of Applied Science and Technology (UAST) - Misagh, Simin Dasht, Karaj, Iran.
Masood Rezaeizadeh
Department of Mechanical Engineering, Graduate University of Advanced Technology, Kerman, Iran.